SIRION®

PRODUCT APPEARANCE MELTING RANGE         PARTICLES SIZE DESCRIPTION TDS
VP 1016 light yellow flakes 105 – 117 °C < 2 mm Matting agent for powder coatings based on triglycidylsocyanature and epoxy/polyester hybrids
VP 1035 light yellow flakes 80 – 100 °C < 180 μm Matting agent for powder coatings based on epoxy/polyester hybrids
VP 1110 white flakes 80 – 100 °C < 2 mm Accelerator to increase the reactivity in hybrids, polyester/TGIC, polyester/epoxy ester
VP 1115 white flakes 80 – 100 °C < 8 mm Additive indicated to prevent yellowing of powder coatings during curing in presence of N0x (gas oven)

PRODUCT GARDNER VISCOSITY AT 25°C MELTING RANGE                HYDROXYL EW (g/eq) REACTIVITY TG DESCRIPTION TDS
VP 2080 H-M 60 – 70°C < 250 +/- 30 ‘+’ 54

Phenolic Hardener based on unmodified solid reaction product of liquid epoxy resin

(LER) and BPA containing a polyacrylate flow modifier and curing accelerator. Designed for Powder Coating is totally compatible with Epoxy Resins.
Preferred application for good flow decorative, protective and high gloss powder coating.
Moderate reactivity.

Read more
VP 2081 H-M 60 – 70°C < 250 +/- 31 ‘++’ 50 Phenolic Hardener based on unmodified solid reaction product of liquid epoxy resin
(LER) and BPA containing a polyacrylate flow modifier and curing accelerator. Designed for Powder Coating is totally compatible with Epoxy Resins.
Preferred application for good flow decorative, protective and high gloss powder coating.
Medium reactivity.

Read more
VP 2082 H-M 60 – 70°C < 250 +/- 32 ‘+++’ 50 Phenolic Hardener based on unmodified solid reaction product of liquid epoxy resin
(LER) and BPA containing a polyacrylate flow modifier and curing accelerator. Designed for Powder Coating is totally compatible with Epoxy Resins. Can be formulated into protective or decorative powder coating. Relative high reactivity.
Read more
VP 2083 H-M 60 – 70°C < 250 +/- 33 ‘++++’ 47 Phenolic Hardener based on unmodified solid reaction product of liquid epoxy resin
(LER) and BPA containing a polyacrylate flow modifier and curing accelerator. Designed for Powder Coating is totally compatible with Epoxy Resins. Very high reactivity.

Read more
VP 2084 H-M 60 – 70°C < 250 +/- 34 ‘++’ 50 Phenolic Hardener based on unmodified solid reaction product of liquid epoxy resin
(LER) and BPA containing curing accelerator.
Designed for Powder Coating is totally compatible with Epoxy Resins. Can be formulated into protective or decorative powder coating. Medium reactivity.

Read more
VP 2085 H-M 60 – 70°C < 250 +/- 35 ‘++++’ 52 Phenolic Hardener based on unmodified solid reaction product of liquid epoxy resin
(LER) and BPA. Designed for Powder Coating is totally compatible with Epoxy Resins. Can be formulated into protective or decorative powder coating. The product contain no curing accelerator and no flow modifier. It is useful for optimizing the reactivity of powder coating formulation which already contain a curing accelerator

Read more

PRODUCT ACID NUMBER (mg KOH/g r) SOLID CONTENT (%) SOLVENT DESCRIPTION TDS
VP 1080 C 40 170-210 40 Cyclohexanone In combination with high MW epoxy resins is suitable for can&coil coatings. It provides very high chemical and thermal resistance. FDA 21 CRF 175.300 and 10/2011 CE compliant

PRODUCT BROOKFIELD (C&P) VISCOSITY                  SOLID CONTENT DESCRIPTION TDS
VP 1030 1000-3000 at 150°C >98% Homopolymer of butyl acrylate. Flow and levelling agent. Indicated for the preparation of polyester resins and solid epoxy resins masterbatches
VP 1040 2000 at 75°C / 800 at 100°C > 98,5% Higher MW of VP 1030  

Epoxy systems

PRODUCT SUGGESTED AMOUNT         DESCRIPTION TDS
2501 0,2 – 1% on total formulation Silicone-free defoamer and air release agent for solvent and solvent-free coatings
2524 0,1 – 1% on total formulation Defoamer and air relaese agent for water based coatings
2530 0,4 – 1% on total formulation Silicone-free defoamer and air release agent for solvent and solvent-free coatings
2541 0,2 – 1% on total formulation Silicone-free defoamer and air release agent for solvent and solvent-free coatings
2705 0,5 – 2% on total formulation Wetting and dispersing additive for epoxy filled resins.

Polyester and FRP

PRODUCT SOLID CONTENT DENSITY AT 25°C (g/ml) DOSAGE DESCRIPTION TDS
FG 1055 8,5 0,87 0,1 – 1% based on total mixture quantity Silicone-free, anti-foam polymer-based additive for wood coatings
FG 1550 10 0,87 0,1 – 0,5% based on resin quantity Silicone-free, anti-foam polymer-based additive
FG 1555 40 0,88 0,1 – 0,5% based on resin quantity Silicone-free, anti-foam polymer-based additive
FG 3706 50 – 0,5 – 1,5% based on resin quantity Solution of polyacrylate. Flow agent for UPR, PU and solvent-free epoxy
FG 1740 – – 0,2 – 0,7% based on resin quantity Styrene-emission reduced additive for orthophtalic polyester resins
FG 1750 – – 0,2 – 1% based on resin quantity Styrene-emission reduced additive for isophtalic & DCPD polyester and vinylester resins
FG 3909 – – 0,5 – 1,5% based on filler quantity Solution of boric acid ester. Wetting and dispersing additive for UPR